Stainless steel ball

Material:AISI304,316,420C,440C Size:0.8mm-150mm Grade: G10-G1000 Standard:ISO 9001:2008/SGS test report/ROHS report

Stainless steel ball

Name: Stainless steel balls

Material: AISI304,316,420C,440C

Size: 0.8mm-150mm

Grade:  G10-G1000

Hardness: AISI304 and AISI316 are soft materials. For AISI420C after heat-treatment, the hardness is between HRC54-60. For AISI440C is HRC58-62

Quality standard: ISO 9001:2008/SGS test report/ROHS report

Feature&Applications:

ss 304 stainless steel ball is the most widely used in the market,it can be used in iatrical instruments,chemical industry,plastic hard ware,scent bottle sprayer,valve,nail polish,air condition,medical material,automotive fittings.

Material Composition %

Material	C	Si	Mn	P	S	Ni	Cr	Mo
AISI304	0.07 max	1.0 max	2.0 max	0.045 max	0.03 max	8.0-10.5	17.0-19.0
AISI316	0.07 max	1.0 max	2.0 max	0.045 max	0.03 max	10.0-14.0	16.5-18.5	2.00-2.50
AISI420C	0.40-0.50	1.0 max	1.0 max	0.04 max	0.03 max	1.0 max	12.0-14.0
AISI440C	0.95-1.20	1.0 max	1.0 max	0.04 max	0.03 max	0.60 max	16.0-18.0	0.40-0.80

Appications:

440C Stainless steel is a type of modern steel and famous for its high corrosion resistant, wear resistance, strength and hardness qualities among all the stainless alloys, capable of attaining (after heat treatment) the highest hardness (60 HRC). It has good resistance to the atmosphere, fresh water and mild acids. It has best resistance in the hardened, tempered and passivated condition. It allows creating a smooth polished surface and Razor sharp edges. It is being used in rolling element bearings, valve seats, casters, ball bearings and valve parts.

420C is a martensitic stainless steel with 12% Chromium which is sufficient to give good corrosive resistance properties. .It’s best corrosive resistance is when hardened and surface is ground or polished. It has good ductility in the annealed condition but can be hardened up to 500HB (highest of the chromium grades) due to its excellent harden-ability, it is capable of getting hardened up to 56 HRC Rockwell or higher. Martensitic Grades are known for high hardness and allowances must be made for poor weld ability and usually allowances for a final harden and temper treatment. 420 steel is magnetic and welding is not recommended. Material will not pass the 72 hours salt bath test.

316  is Austenitic stainless steel with features similar to AISI 302/304/304L series, but they can be anti-magnetic and, above all, the addition of molybdenum offers greater chemical resistance, particularly in sulfuric acid concentration. All balls can be annealed and passivated. The most common applications include their use in the chemical, paper and textile industries (valves, pumps and bearings).

OUR MAIN PRODUCTS:

Stainless steel ball:AISI302,304,316,420,4440C

Bearing steel balls:AISIE52100

Carbon steel balls:AISI1010,1015,1045,1085

Steel shot:S70,S110,S130,S170,S230,S280,S330,S390,S460,S550,S660,S780,S930

Steel Grit:G120,G80,G50,G40,G25,G18,G16,G14,G12,G10

Any further Information,

Plz contact us!

Stainless steel ball